Beneficial effects of ethyl-cyanoacrylate coating against candida albicans biofilm formation

Abstract The aim of this study was to verify whether modifications made in a hard chairside reline resin by an ethyl-cyanoacrylate adhesive, ECA (Super Bonder®, Loctite, Itapevi, SP, Brazil) would be able to inhibit or reduce Candida albicans biofilm formation on its surface, comparing to a commercial surface sealant (BisCover®, Bisco, Schaumburg, USA). Reline resin specimens were fabricated and randomly divided into 6 groups (n=8): CG (control group), no surface treatment; ECA1, ECA coating on the surface before sterilization; ECA2, ECA coating after sterilization; ECA3, ECA incorporated in the resin bulk; DPE1, BisCover® coating before sterilization; DPE2, BisCover® coating after sterilization. Specimens were inoculated with C. albicans SC5314 (1x107 cells/mL) and incubated for 24 h. Then, the biofilm were stained with LIVE/DEAD® BaclightTM L7007 Kit and analyzed by Confocal Laser Scanning Microscopy. The images were evaluated by bioImageL® v.2.0 software and total biovolume (µm3), viable cells (%), and covered area (%) were calculated. Data were statistically analyzed by Kruskal-Wallis and Dunn tests (p<0.05). Results showed that ECA-coated groups presented better results, reducing C. albicans biofilm formation. Acquired images revealed that these groups (ECA1 and ECA2) presented a reduced number of cells, mostly in yeast form (less pathogenic), while the other groups presented higher number of cells, mostly in hyphae form (more pathogenic). Based on these findings, a beneficial effect of Super Bonder® coating reline resins surface could be demonstrated, suggesting a promising way to prevent fungal biofilm formation on dentures.

Resumo O objetivo deste estudo foi verificar se as modificações feitas com o adesivo etil cianoacrilato, ECA (Super Bonder ®, Loctite, Itapevi, SP, Brasil) sobre as resinas acrílicas para reembasamento, poderiam inibir ou reduzir a formação de biofilmes de C.albicans sobre sua superfície quando comparado com um selante de superfície comercial (BisCover®, Bisco, Schaumburg, EUA). Amostras de resina acrílica para reembasamento foram fabricadas e divididas aleatoriamente em 6 grupos (n=8): CG (grupo controle), sem tratamento superficial; ECA1, revestimento de ECA na superfície antes da esterilização; ECA2, revestimento de ECA após esterilização; ECA3, ECA incorporado no volume da resina; DPE1, revestimento de BisCover® antes da esterilização; DPE2, revestimento de BisCover® após esterilização. Os espécimes foram inoculados com C. albicans SC5314 (1x107 células/mL) e incubados durante 24 h. Seguidamente, o biofilme foi corado com LIVE/DEAD® BaclightTM L7007 Kit e analisado no microscópio confocal de varredura a laser. As imagens foram avaliadas pelo software bioImageL® v.2.0, no qual foram calculados o biovolume total (μm3), as células viáveis (%) e a área coberta (%). Os dados foram analisados estatisticamente pelos testes de Kruskal-Wallis e Dunn (p<0,05). Os resultados mostraram que os grupos revestidos com ECA apresentaram os melhores resultados, reduzindo a formação do biofilme de C. albicans. As imagens adquiridas revelaram que esses grupos (ECA1 e ECA2) apresentaram um número reduzido de células, principalmente na forma de levedura (menos patogênico), enquanto os outros grupos apresentaram um maior número de células, principalmente na forma de hifas (mais patogênicas). Com base nessas descobertas, encontra-se um efeito benéfico na aplicação do adesivo ECA sobre as superfícies das resinas acrílicas para reembasamento, sugerindo assim uma nova alternativa de prevenir a formação de biofilme fúngico em próteses dentárias.

Efeito do etil-cianoacrilato (Super Bonder®) e do polidor líquido de baixa viscosidade (Biscover®) sobre biofilme de Candida albicans em resina acrílica para reembasamento / Effect of ethyl-cyanoacrylate (Super Bonder®) and a liquid polish of low viscosity (Biscover®) on Candida albicans biofilms on denture reline resin

A proposta desse trabalho foi verificar através de microscopia confocal de varredura a laser, se a utilização de uma resina fotopolimerizável de baixa viscosidade (Biscover®) e do etil-cianoacrilato (Super Bonder®) seriam eficientes em prevenir ou reduzir a formação de biofilme de Candida albicans. Cinqüenta e seis corpos de prova em resina acrílica para reembasamento (New Truliner) foram divididos aleatoriamente em 7 grupos: G1 (C)- Controle; G2 (SBAE)- Recebeu uma camada de Super Bonder® em sua superfície antes de esterilizar; G3 (SBDE)- Recebeu uma camada de Super Bonder® em sua superfície depois de esterilizar; G4 (SB3G)- 3 gotas de Super Bonder® incorporadas na resina; G5 (SB4G)- 4 gotas de Super Bonder® incorporadas na resina; G6 (BCDE)- Recebeu uma camada de Biscover® em sua superfície depois de esterilizar e G7 (BCAE) Recebeu uma camada de Biscover® em sua superfície antes de esterilizar. Todos os corpos de prova foram inoculados com Candida albicans para formação de biofilme. Os biofilmes remanescentes sobre os corpos de prova foram corados através dos fluorocromos SYTO-9 e iodeto de propídeo para análise no microscópio confocal. Os dados foram analisados através dos testes estatísticos de Kruskal-Wallis e Dunn, a um nível de significância de 5%. Os resultados obtidos pelo microscópio confocal mostraram que, de todos os corpos de prova modificados, os que receberam a Super Bonder® em sua superfície, G2(SBAE) e G3(SBDE) foram os únicos que significativamente reduziram a formação de biofilme de Candida albicans. Através da análise das imagens geradas pelo microscópio confocal, pôde-se observar que nos grupos G2(SBAE) e G3(SBDE) os campos apresentaram um reduzido número de células fúngicas e a maioria se encontrava na forma de levedura (inócua), enquanto que, para os demais grupos, além de observado um elevado número de células, a maioria destas se apresentava em forma de hifa (patogênica). Desse modo, a partir das...

The purpose of this study was to verify, using the confocal laser scanning microscopy (CLSM), if the use of a photoactivated resin of low viscosity (Biscover®) and a ethyl-cyanoacrylate (Super Bonder®) could be efficient in the prevention or reduction of Candida albicans biofilms. Fifty six reline resin specimens (New Truliner) were fabricated and randomly divided into 7 groups: G1 (C)- Control; G2 (SBAE)- a Super Bonder® layer was applied on the surface before sterilization; G3 (SBDE)- the surface received a Super Bonder® layer after sterilization; G4 (SB3G)- 3 drops of Super Bonder® were incorporated in the structure of the resin; G5 (SB4G)- 4 drops of Super Bonder® were incorporated in the structure of the resin; G6 (BCDE)- a Biscover® layer was applied on the surface after sterilization; G7 (BCAE) the surface received a Biscover® layer before sterilization. All the specimens were inoculated with Candida albicans for biofilm dvelopment. The remaining biofilms on the specimens were stained with fluorochromes SYTO-9 and propidium iodide to be analyzed by CLSM. The data were statistically analyzed using the Kruskal-Wallis and Dunn test, considering a significance level of 5%. The data obtained by CLSM revealed that of all specimens modified, those that received a Super Bonder® layer on their surface, G2(SBAE) e G3(SBDE), presented the better results, reducing Candida albicans biofilm formation. Analyzing the images produced by CLSM it was possible to see that groups G2(SBAE) e G3(SBDE) showed a reduced number of cells, and they were in a less phatogenetic form (Yeast), while the other groups showed a high number of cells in a more pathogenetic form (Hyphae). Considering the experimental conditions of this study we can conclude that the material modifications done with Super Bonder® on the surface could be an interesting way to prevent or control biofilm formation on acrylic resin.

Efeito do etil-cianoacrilato (Super Bonder®) e do polidor líquido de baixa viscosidade (Biscover®) sobre biofilme de Candida albicans em resina acrílica para reembasamento / Effect of ethyl-cyanoacrylate (Super Bonder®) and a liquid polish of low viscosity (Biscover®) on Candida albicans biofilms on denture reline resin

A proposta desse trabalho foi verificar através de microscopia confocal de varredura a laser, se a utilização de uma resina fotopolimerizável de baixa viscosidade (Biscover®) e do etil-cianoacrilato (Super Bonder®) seriam eficientes em prevenir ou reduzir a formação de biofilme de Candida albicans. Cinqüenta e seis corpos de prova em resina acrílica para reembasamento (New Truliner) foram divididos aleatoriamente em 7 grupos: G1 (C)- Controle; G2 (SBAE)- Recebeu uma camada de Super Bonder® em sua superfície antes de esterilizar; G3 (SBDE)- Recebeu uma camada de Super Bonder® em sua superfície depois de esterilizar; G4 (SB3G)- 3 gotas de Super Bonder® incorporadas na resina; G5 (SB4G)- 4 gotas de Super Bonder® incorporadas na resina; G6 (BCDE)- Recebeu uma camada de Biscover® em sua superfície depois de esterilizar e G7 (BCAE) Recebeu uma camada de Biscover® em sua superfície antes de esterilizar. Todos os corpos de prova foram inoculados com Candida albicans para formação de biofilme. Os biofilmes remanescentes sobre os corpos de prova foram corados através dos fluorocromos SYTO-9 e iodeto de propídeo para análise no microscópio confocal. Os dados foram analisados através dos testes estatísticos de Kruskal-Wallis e Dunn, a um nível de significância de 5%. Os resultados obtidos pelo microscópio confocal mostraram que, de todos os corpos de prova modificados, os que receberam a Super Bonder® em sua superfície, G2(SBAE) e G3(SBDE) foram os únicos que significativamente reduziram a formação de biofilme de Candida albicans. Através da análise das imagens geradas pelo microscópio confocal, pôde-se observar que nos grupos G2(SBAE) e G3(SBDE) os campos apresentaram um reduzido número de células fúngicas e a maioria se encontrava na forma de levedura (inócua), enquanto que, para os demais grupos, além de observado um elevado número de células, a maioria destas se apresentava em forma de hifa (patogênica). Desse modo, a partir das...

The purpose of this study was to verify, using the confocal laser scanning microscopy (CLSM), if the use of a photoactivated resin of low viscosity (Biscover®) and a ethyl-cyanoacrylate (Super Bonder®) could be efficient in the prevention or reduction of Candida albicans biofilms. Fifty six reline resin specimens (New Truliner) were fabricated and randomly divided into 7 groups: G1 (C)- Control; G2 (SBAE)- a Super Bonder® layer was applied on the surface before sterilization; G3 (SBDE)- the surface received a Super Bonder® layer after sterilization; G4 (SB3G)- 3 drops of Super Bonder® were incorporated in the structure of the resin; G5 (SB4G)- 4 drops of Super Bonder® were incorporated in the structure of the resin; G6 (BCDE)- a Biscover® layer was applied on the surface after sterilization; G7 (BCAE) the surface received a Biscover® layer before sterilization. All the specimens were inoculated with Candida albicans for biofilm dvelopment. The remaining biofilms on the specimens were stained with fluorochromes SYTO-9 and propidium iodide to be analyzed by CLSM. The data were statistically analyzed using the Kruskal-Wallis and Dunn test, considering a significance level of 5%. The data obtained by CLSM revealed that of all specimens modified, those that received a Super Bonder® layer on their surface, G2(SBAE) e G3(SBDE), presented the better results, reducing Candida albicans biofilm formation. Analyzing the images produced by CLSM it was possible to see that groups G2(SBAE) e G3(SBDE) showed a reduced number of cells, and they were in a less phatogenetic form (Yeast), while the other groups showed a high number of cells in a more pathogenetic form (Hyphae). Considering the experimental conditions of this study we can conclude that the material modifications done with Super Bonder® on the surface could be an interesting way to prevent or control biofilm formation on acrylic resin.